Marrakai:

Have you tried heat treating wheelweights? I have had success merely dropping the bullets straight from the mold into a bucket of water. After a few days they feel like copper to the "tooth test".

I am curious if wheelweights Down Under are the same or similar alloy to ours? Dunno.

The other question is, what would you think of using straight wheelweights for Sarg's buff? Certainly not as hard as HT'd WW's, but harder than lead, and not brittle either, though in a 12 br ball I don't think brittleness would be a real factor.

When I get old and my bones are creaky and I just can't handle winter anymore, I want to sell the ranch and move over there. You WB's are just too tempting...