That's cool.; I would never have thought 50/50 solder would be good enough to seal the pressure at the base. I'd have used hard (high temp) silver solder on a short rod that fit properly. A .001" (1 mil) (not mm))joint would have very much more strength than needed.
Perhaps due to the tiny hole, more strength is not needed.