CFA,

Glad to hear that you are back in action with a "new" H&H .500/.465.

I have recently been advised by Woodleigh that it is a good idea to have the barrels hardness tested and that anything at or above a 220 Vickers reading should be fine with any but monolithic solids (meaning, I think, straight shanked monolithics, as opposed to proper diameter grooved models).